樂泰 HYSOL KL 1000-4T provides the lowest cost ofownership with superior moldability and reliability.
This materialis designed to achieve JEDEC Level 4 requirements, at 220°C reflow temperature.
樂泰 HYSOL KL 1000-4T meets UL 94 V-0 Flammabilityat 3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 23 Spiral Flow, @ 175°C, cm 85Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATAHandling Preheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 20Automold, seconds 4 to 10Curing Time, @ 175oC:Conventional mold, seconds 60 to 120Automold, seconds 50 to 80Post Cure @ 175°C, hours 4 to 6樂泰 HYSOL KL 1000-4T has been formulated to provide thebest possible moldability and as wide a molding latitude as possible.
Although molding and curing conditions will vary from situation tosituation, recommended starting ranges are shown aboveStorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.
Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers.
After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.
樂泰 HYSOL KL 1000-4T提供*低的擁有成本，具有出色的成型性和可靠性。
這種材料設計用于在220°C達到JEDEC 4級要求回流溫度.樂泰 HYSOL KL 1000-4T滿足UL 94 V-0 Flammabilityat 3.175mm厚度。
固化材料的特性特性時間@ 175°C秒秒23螺旋流，@ 175°C，cm 85Shelf壽命：@5oC，天365工藝流程數據處理預熱溫度：常規模具，°C 80至100Automold，秒0至5模具溫度，℃150至195模壓，Kg /cm240至100轉印時間：常規模具秒10至20Auoldold秒秒4至10℃恒定時間@ 175℃：常規模具，秒60至120Automold，秒50至80固化@ 175°C，小時4至6樂泰 HYSOL KL 1000-4T已經配制，以提供盡可能*高的成型性和更寬的成型緯度。