MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/MACROMELT OM633電子組裝/工業膠水/電子組裝膠水/工業用膠
技術服務熱線：021-51693135 / 021-22818476
TECHNOMELT PA 633 high performance thermoplastic polyamide
is designed to meet low pressure molding process requirements. This
product can be processed at low processing pressure due to its low
viscosity, allowing encapsulation of fragile components without
damage.
LIQUID-STATE TYPICAL PROPERTIES
Viscosity @ 210 °C, mPa∙s (cP) 3,500
Specific Gravity @ 25 °C 0.98
Softening Point, °C 170 to 180
TYPICAL PROCESS DATA
Handling:
Molding Temperature, °C 200 to 240
TECHNOMELT PA 633 has been formulated to provide the best
possible moldability and as wide a molding latitude as possible. Much
of the final molding parameters will be determined by the mold design.
Although molding and curing conditions will vary from situation to
situation, recommended starting ranges are shown above.
Storage
Store product in the unopened container in a dry location. Storage
information may be indicated on the product container labeling
TECHNOMELT PA 633高性能熱塑性聚酰胺
旨在滿足低壓成型工藝要求。這個
產品可以在低加工壓力下進行處理，因為其低
粘度，允許無脆性組分的包封
損傷。
液態典型特性
粘度@ 210℃，mPa•s（cP）3,500
比重@ 25°C 0.98
軟化點，℃170至180
典型工藝數據
處理：
成型溫度，°C 200〜240
TECHNOMELT PA 633已經被制定為提供*好的
可能的成型性和盡可能寬的成型緯度。許多
的*終成型參數將由模具設計確定。
雖然成型和固化條件將因情況而異
情況，推薦的起始范圍如上圖所示。
存儲
將產品 |