ESTANE ZHF 92AT8 TPU
Technical Data Sheet Type: ESTANE廬 ZHF 92AT8 NAT 01 is a non-halogen, flame retardant, aromatic polyether-based thermoplastic polyurethane. Application: Extrusion 鈥� Based on extruded strips 鈥� Prior to testing samples were conditioned at 23擄C for 24 hours 鈥� Listed values are 鈥渢ypical (average) values鈥� and should/can not be applied for specification purposes. Supply Form and Standard Packaging 鈥� ESTANE廬 ZHF 92AT8 NAT 01 is supplied in pellet form and packaged in 25 kg (x lb) bags or 700-800 kg boxes (xy lbs). Material Preparation 鈥� Prior to processing, ESTANE廬 ZHF 92AT8 NAT 01 must be dried at 100潞C for 3-4 hours. 鈥� It is recommended to dry the material in a vacuum or dehumidifying type dryer. Target dew point should be -40擄C. 鈥� Depending on the applied processing technique, the maximum moisture level should be 0.02%. Physical Properties Value (Metric) Unit Test Method Hardness A/1: 94 Shore A ISO 868 Specific Gravity 1.22 g/cm3 ISO 1183 Tensile Strength 15 MPa VDE282 part 10 Ultimate Elongation 502 % VDE282 part 10 Tensile Stress at: - 100 % Elongation 8 MPa VDE282 part 10 - 300 % Elongation 10 MPa VDE282 part 10 Tear Strength nicked 72 kN/m ISO 34-1B Application Specific Properties Value (Metric) Unit Test Method UL Flame Rating V0-2 mm - UL-94 LOI 34 % ASTM D-2863 Smoke Density (0.75 mm) - Flaming DM Non flaming DM ASTM E6 |
免責聲明：以上所展示的信息由會員自行提供，內容的真實性、準確性和合法性由發布會員負責，www.qy6.com對此不承擔任何責任。如有侵犯您的權益，請來信通知刪除。