PRODUCT DESCRIPTIONHysol®MG15F-R is an anhydride cured molding compound designed for use in high voltage power applications requiringgood electrical stability at high temperature. The material isspecifically recommended for Power Discrete, High VoltageRectifier, and other applications where traditionally, Siliconemolding compounds have been the product of choice.PROPERTIES OF UNCURED MATERIALColor Black Spiral Flow, @ 177oC, cm 66Ram Follower Gel Time, seconds 8Shelf Life @ 5oC, months 12 TYPICAL CURED PROPERTIESAll measurements taken at 21oC unless otherwise noted. All
physical, electrical and analytical measurements taken onspecimens cured for two minutes at 190oC with post cure of 4hours at 200oC, unless otherwise specified.Glass Transition Temperature, °C, STP 65B 190Coefficient of Thermal Expansion, cm/cm/oC50o - 100oC, x 10-6 23250o - 260oC, x 10-6 71Specific Gravity 1.80Molded Shrinkage, as molded, % 0.5
Flexural Strength, kg/mm2 11.5Flexural Modulus, kg/mm2 1550Thermal Conductivity, CGS units, x 10-4 17Flammability Rating @ 3mm thickness V-0Moisture Absorption, 1 Atm steam, %100 hours 1.01000 hours 1.4Volume Resistivity, 500 volts, ohm-cm@ 21oC 1.5 x 1016@ 100oC 1.4 x 1015100 hours @ 15 psi 1.5 x 1016Water Extract Data, 1.5 hour water boil,conductivity, micromhos 20pH of extract 4.5chloride content, ppm 20sodium content, ppm 20HANDLINGMG15F-R has been formulated to provide the best possiblemoldability and as wide a molding latitude as possible.Although molding and curing conditions will vary from situation
產品描述Hysol®MG15F-R是酸酐固化的模塑料設計用于需要高溫下良好電氣穩定性的高壓電源應用。該材料特別推薦用于Power Discrete，High VoltageRectifier以及其他傳統上使用Siliconemolding化合物作為選擇產品的應用.PRESSER OF UNCURED MATERIALColor Black螺旋流量，@177oC，cm 66Ram隨機凝膠時間，秒8Shelf Life @5oC，月12典型固化性能除非另有說明，否則在21oC下進行所有測量。
所有物理，電氣和分析測量取決于在190oC下固化2分鐘，在200oC下后固化4小時，除非另有說明。玻璃轉變溫度°C，STP 65B 190熱膨脹系數，cm / cm /oC50o-100oC，x 10 -623250o - 260oC，x 10-6 71特殊重力1.80模壓收縮率，％0.5彎曲 |