樂泰 HYSOL GR 2811 epoxy molding compound deliversoutstanding performance and ease of use.
This material isdesigned to achieve JEDEC Level 1 requirements, at 260°C eflow temperature.樂泰 HYSOL GR 2811 meets UL 94 V-0 Flammability at6.35mm thickness.TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 15Spiral Flow, @ 177°C, inches 34Shelf Life:@ -4oC, days 183TYPICAL PROCESS DATA
HandlingPreheat Temperature , °C 80 to 95Molding Temperature, °C 140 to 180Transfer Pressure, Kgf/cm2 40 to 85Transfer Time, seconds 6 to 15Curing Time, :@ 177oC, seconds 30 to 45Curing Time, 3 mm section:Conventional mold:@ 175oC, seconds 40 to 70
Automold:@ 175oC, seconds 30 to 60Post Cure @ 175°C, hours 2 to 6StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at -4oCor below, in closed containers.
After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisture
contamination. The suggested waiting time for a standard 15kg carton box is 24 hours.
樂泰 HYSOL GR 2811環(huán)氧樹脂模塑料具有出色的性能和易用性。
該材料設(shè)計(jì)為在260°C達(dá)到JEDEC 1級(jí)要求回流溫度.樂泰 HYSOL GR 2811符合UL 94 V-0可燃性在6.35mm厚度。
固化材料的特性特性時(shí)間@ 175°C，秒15螺旋流，@ 177°C，英寸34Shelf壽命：@-4oC，天183工藝數(shù)據(jù)處理預(yù)熱溫度，°C 80至95模具溫度，°C 140至180轉(zhuǎn)印壓力Kgf /cm240至85轉(zhuǎn)印時(shí)間秒6至15℃固化時(shí)間：177℃，秒30至45℃固化時(shí)間，3毫米截面：常規(guī)模具：@ 175℃秒40至70Automold：@175oC，秒30至60固化@ 175°C，小時(shí)2至6個(gè)儲(chǔ)存在未開封的容器中的產(chǎn)品在干燥的位置。
儲(chǔ)存信息可能在產(chǎn)品容器標(biāo)簽上指示。粉末儲(chǔ)存 - 粉末或預(yù)制件應(yīng)存放在 - 4oC以下，在密閉容器中。從冷藏箱中取出后，必須在密封容器中允許材料進(jìn)入室溫，以避免潮濕污染。
標(biāo)準(zhǔn)15kg紙箱的建議等待時(shí)間為24小時(shí)。 |