漢高漢高樂泰樂泰 3707
技術服務熱線：021-51693135 / 021-22818476
樂泰 3707 UV curable edgebond is designed for bonding various types of electronic components on a PCB.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity, Brookfield CP52, 25 °C, mPa•s (cP):
Speed 20 rpm 9,595
Pot Life @ 25oC, days <7
Shelf Life - Refer to package label
Flash Point - See SDS
TYPICAL CURING PERFORMANCE
Recommended UV Cure
>3,000mJ or
>30 seconds @ 100 mW/cm2
Cure Depth, mm:
MPHL (UVALoc1000) at 100 mW/cm2, for 30 seconds ≥10
Oven Cure
2 minute @ 130°C
Minimum intensity of 100 mW/cm2 is recommended for the UV lamp. Use suggested cure schedules as general guidelines; other cure schedules may yield satisfactory results.
The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Specimen was prepared by thermal cure only
Physical Properties
Coefficient of Thermal Expansion , ppm/°C:
Below Tg 52
Above Tg 151
Glass Transition Temperature (Tg) by TMA, °C 53
Storage Modulus, GPa 4.4
樂泰3707 UV edgebond設計結合各類電子元件在PCB。
固化材料的典型性能
粘度，Brookfield cp52，25°C，MPA•S（CP）：
速度20轉9595
鍋生活@ 25oC、d＜7
貨架壽命-參考包裝標簽
閃點-見SDS
典型的固化性能
推薦固化
> 3000mj或
> 30秒@ 100毫瓦/厘米2
固化深度，采購經理：
MPHL（uvaloc1000）在100毫瓦/厘米2，30秒≥10
烘箱中固化
2分鐘@ 130°C
*小強度為100毫瓦/厘米2推薦用于紫外燈。使用建議的治療時間表作為一般指導方針，其他治療方案可能會產生令人滿意的結果。
上述固化型材指南建議。固化條件（時間和溫度）可能會根據客戶的經驗和他們的應用要求，以及客戶固化設備，烘箱負荷和實際烤箱溫度變化。
固化材料的典型性能
標本僅通過熱固化制備
物理性質
熱膨脹系數，PPM /°C：
在Tg 52
在Tg 151
玻璃化轉變溫度（Tg）通過TMA，°C 53
儲能模 |