樂泰 HYSOL GR 2710 epoxy molding compound deliversoutstanding performance and ease of use.
樂泰 HYSOL GR 2710 meets UL 94 V-0 Flammability at6.35mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 15Spiral Flow, @ 177°C, cm 88.9Shelf Life:@ 5oC, days 365Hot Hardness,Shore-D@ 175°C, 90 seconds 85TYPICAL PROCESS DATAHandlingPreheat Temperature , °C 80 to 95Molding Temperature, °C 140 to 180Transfer Pressure, Kgf/cm2 40 to 85Transfer Time, seconds 6 to 15Curing Time, :@ 177oC, seconds 45 to 60Curing Time, 3 mm
section:Conventional mold:@ 175oC, seconds 70 to 90Automold:@ 175oC, seconds 50 to 70Post Cure @ 175°C, hours 2 to 6StorageStore product in the unopened container in a dry location.
Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 10oC or below, in closed containers.
After removal from cold
storage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.
樂泰 HYSOL GR 2710環氧樹脂模塑料具有出色的性能和易用性.
樂泰 HYSOL GR 2710符合UL 94 V-0可燃性，厚度為6.355mm。固化材料的典型特性時間@ 175°C秒秒15螺旋流量，@ 177°C，cm 88.9Shelf壽命：@5oC，365天硬度，Shore-D @ 175°C，90秒85特殊工藝數據處理預熱溫度，°C 80至95模壓溫度，°C 140至180轉印壓力Kgf /cm240至85轉印時間秒6至15凝固時間：177℃，秒45至60℃烘烤時間3毫米截面：常規模具：@ 175℃，秒70至90Automold： @175oC，秒50至70后固化@ 175°C，小時2至6儲存在未開封容器中的產品在干燥的位置。
儲存信息可能在產品容器標簽上指示。粉末儲存 - 粉末或預制件應存放在10oC或更低，在封閉的容器中。從寒冷除去后
儲存時，必須在密封容器中允許材料進入室溫，以避免水分污染。
建議的等待時間為標準15kg紙箱是24小時。 |