ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/ELECTRODAG 6017SS電子組裝/工業膠水/電子組裝膠水/工業用膠
技術服務熱線：021-51693135 / 021-22818476
Electrodag 6017SS screen printable ink is specificallydesigned for blending with Electrodag PM-404 to provideexceptional resistance in the production of low voltage circuitryon polyester film.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Solids Content by Weight, % 25.5 to 28.5
Viscosity, Brookfield , mPa•s (cP):
Speed 20 rpm, @ 20oC 15,000 to 35,000
Density, , Kg/cm3 1,100
Shelf Life @ 5 to 30°C (from date of manufacture), year 1
Flash Point DIN 53213oC 78
TYPICAL SCREEN PRINTING PROCESS
Emulsion Thickness
Emulsion Thickness , μm 20 to 40
Recommended Squeegee
Polyurethane , durometer 70 to 75
Recommended Screen Type
Monofilament polyester screen , threads/cm 61 to 90
Stainless steel screen , threads/cm 77 to 110
The above cure profile is a guideline recommendation. Cure conditions(time and temperature) may vary based on customers' experience andtheir application requirements, as well as customer curing equipment,oven loading and actual oven temperatures. Storage Store product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling. Optimal Storage: 5 to 30 °C . Material removed fromcontainers may be contaminated during use. Do not returnproduct to the original container. 漢高 Corporation cannotassume responsibility for product which has beencontaminated or stored under conditions other than thosepreviously indicated.