樂泰 3220 is designed for use in heat sensitive devices.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Casson Viscosity @ 25 °C, mPa∙s (cP):
Haake PK 100, M10/PK 1 2° Cone 2,500
Viscosity, Brookfield CP51, 25 °C, mPa•s (cP):
Speed 20 rpm 7,150
Thixotropic Index, Brookfield (2/20 rpm) 3.3
Yield Point @ 25°C, MPa 57,000
Specific Gravity 1.36
Pot Life @ 25oC, days >14
Shelf Life @ -15°C (from date of manufacture), days 365
Flash Point - See SDS
TYPICAL CURING PERFORMANCE
Cure Schedule
5 to 10 minutes @ 80°C
With all curing systems, the time required for cure depends on the rate of heating. Cure rate depends on the mass of material to be heated and intimate contact with the heat source. Use suggested cure conditions as general guidelines. Other cure conditions may yield satisfactory results.
The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties :
Volumetric Shrinkage on Cure, % 4.1
Linear Shrinkage on Cure, % 1.3
Hardness, Shore D, ASTM D2240 79
Coefficient of Thermal Expansion :
alpha 1, <Tg ,cm/cm°C 61×10-6
alpha 2, >Tg, cm/cm°C 171×10-6
Glass Transition Temperature (Tg) by TMA
(ITM65B), °C
26
Water Absorption, ASTM D 570 , %:
168 hours @ 85°C/85% RH 2.6
Tensile Modulus, Sample cured 30 minutes @ 80°C:
@ 25oC N/mm2 3,240
(psi) (469,920)
@ 85oC N/mm2 22
(psi) (3,190)
Tensile Strength, ASTM-D-790 N/mm2 13
(psi) (1,885)
TYPICAL PERFORMANCE OF CURED MATERIAL
Lap Shear Strength :
Glass Epoxy to Glass Epoxy N/mm2 20.4
(psi) (2,960)