樂泰 HYSOL KL 4000-1T epoxy molding compound deliversoutstanding performance and ease of use.樂泰 HYSOL KL 4000-1T meets UL 94 V-0 Flammabilityat 3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 25Spiral Flow, @ 175°C, cm 85Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATAHandlingPreheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 20Automold, seconds 4 to 10Curing Time, @ 175oC:Conventional mold, seconds 60 to 120
Automold, seconds 50 to 90Post Cure @ 175°C, hours 4 to 6Not for product specifications
The technical data contained herein are intended as referenceonly. Please contact your local quality department forassistance and recommendations on specifications for thisproduct.
StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers. After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination. The suggested waiting time for a standard 15 kg carton box is 24 hours.
樂泰 HYSOL KL 4000-1T環(huán)氧樹脂成型復合材料具有出色的性能和易用性.樂泰 HYSOL KL 4000-1T符合UL 94 V-0 Flammabilityat 3.175mm厚度。
固化時間@ 175°C，秒25螺旋流，@ 175°C，cm 85Shelf壽命：@5oC，天365工藝過程數(shù)據(jù)處理預熱溫度：常規(guī)模具，80至100Automold，秒0至5模具溫度，°C 150至195模壓，Kg / cm 2 40至100轉(zhuǎn)印時間：常規(guī)模具秒10至20Auoldold秒秒4至10℃恒定時間@ 175℃常規(guī)模具秒60至120Automold，秒50至90后固化@ 175°C，小時4至6不適用于產(chǎn)品規(guī)格本文包含的技術(shù)數(shù)據(jù)僅供參考。
請聯(lián)系您當?shù)氐馁|(zhì)量部門，了解本產(chǎn)品的規(guī)格。StorageStore產(chǎn)品在未開封的容器中，在干燥的位置。存儲信息可能在產(chǎn)品容器標簽上指示。粉末儲存 - 粉末或預制件應存放在5oC以下，密閉容器中。
從冷藏箱中取出后，必須在密封容器中使材料達到室溫，以避免水分污染。