TRA-BOND F112 adhesive is formulated for fiber optic assembly applications.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Thixotropic Index 1.0
Viscosity @ 25 °C, mPa∙s (cP):
After Mixing 1,800
Specific Gravity, cured 1.2
Pot Life:
@ 2grams, minutes 30
Work Life:
@ 2grams, hour 1
Flash Point - See MSDS
TYPICAL CURING PERFORMANCE
Cure Schedule
24 hours @ 25°C or
1 hour @ 65°C or
15 minutes @ 90°C
Sufficient cure in 15 minutes @ 65oC is developed for polishing connectors.
The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties:
Coefficient of Thermal Expansion, cm/cm/oC 6.20×10+01
Glass Transition Temperature (Tg), ultimate, °C 102
Hardness, Shore D 86
Refractive Index 1.51
Water Absorption , after 24 hours saturation, % 0.07
tra-bond F112膠光纖裝配應用制定。
固化材料的典型性能
觸變指數1
粘度@ 25°C，MPA∙S（CP）：
混合后的1800
比重，固化1.2
鍋里的生活：
“2grams，30分鐘
工作生活：
“2grams，小時1
閃光點看到MSDS
典型的固化性能
治療計劃
24小時@ 25°C或
1小時@ 65°C或
15分鐘@ 90°C
15分鐘@ 65oC足療用于拋光的連接器。
上述固化型材指南建議。固化條件（時間和溫度）可能會根據客戶的經驗和他們的應用要求，以及客戶固化設備，烘箱負荷和實際烤箱溫度變化。
固化材料的典型性能
物理性質：
熱膨脹系數，厘米/厘米/oC 6.20×10 + 01
玻璃化轉變溫度（Tg），極限，°C 102
硬度，岸上D 86
折射率1.51
吸水，24小時飽和度后，% 0.0 |