樂泰 HYSOL KL 4500-1 epoxy molding compounddelivers outstanding performance and ease of use.
Thismaterial is designed to achieve JEDEC Level 3 requirements,at 260°C reflow temperature.樂泰 HYSOL KL 4500-1 meets UL 94 V-0 Flammability at .175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 25Spiral Flow, @ 175°C, cm 85Shelf Life @ 5oC, days 365TYPICAL PROCESS DATAHandling Preheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 15Automold, seconds 4 to 10Curing Time, @ 175oC:Conventional mold, seconds 60 to 120Automold, seconds 50 to 90Post Cure @ 175°C, hours 4 to 6樂泰 HYSOL KL 4500-1 has been formulated to provide the bestpossible moldability and as wide a molding latitude as possible.
樂泰 HYSOL KL 4500-1環(huán)氧樹脂成型復合材料具有出色的性能和易用性。該材料旨在實現(xiàn)JEDEC 3級要求，溫度為260°C .樂泰 HYSOL KL 4500-1符合UL 94 V-0可燃性，厚度為3.7575mm。固化材料的典型特性時間@ 175°C秒秒25螺旋流@ @ 175°C，cm 85Shelf壽命@5oC，365天工藝流程數(shù)據(jù)處理
預熱溫度：常規(guī)模具，°C 80至100Automold，秒0至5模具溫度，℃150至195壓鑄壓力，Kg /cm240至100轉(zhuǎn)印時間：常規(guī)模具秒10至15Auold，秒4至10℃恒定時間@ 175℃：常規(guī)模具，秒60至120Automold，秒50至90固化@ 175°C，小時4至6樂泰 HYSOL KL 4500-1已經(jīng)配制，以提供盡可能*佳的可模塑性和寬的成型緯度。 |