樂泰 ECCOBOND F 123 is formulated for terminating single or multi-channel fiber optic connectors. 樂泰 ECCOBOND F 123 bonds offer resistance to water and weathering, gasses, petroleum products and other organic and inorganic compounds.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Thixotropic Index 1.0
Viscosity @ 25 °C, cP:
After Mixing 4,000
Specific Gravity, mixed 1.2
Reactive solids contents, % 100
Pot Life , hours 4
Flash Point - See SDS
TYPICAL CURING PERFORMANCE
Cure Schedule
5 minutes @ 100°C
Alternative Cure Schedule
2 minutes @ 120°C or
1 minute @ 150°C
An additional post cure of 30 minutes @ 150oC is recommended when application temperatures higher than 150oC are anticipated.
For masses over 0.25grams, allow material to gel for 4 hours @ 25oC followed by 100oC for 5 hours
The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Coefficient of Thermal Expansion ppm/°C:
Below Tg 6.31×1001
Above Tg 2.03×1002
Glass Transition Temperature (Tg), °C 120
Hardness, Shore D 87
Refractive Index 1.56
Water Absorption, % 0.004
Spectral transmittance (6,000 to 9,000 Å), % 93
Electrical Properties
Dielectric Strength, volts/mil 400
樂泰eccobond F 123是終止單或多通道光纖連接器的制定。樂泰eccobond F 123的債券提供的抗水和抗風化、氣體、石油產品和其它有機和無機化合物。
固化材料的典型性能
觸變指數1
粘度@ 25°C：
混合后的4000
比重，混合1.2
活性固體含量，% 100
鍋壽命，小時4
閃點-見SDS
典型的固化性能
治療計劃
5分鐘@ 100°C
替代治療計劃
2分鐘@ 120°C或
1分鐘@ 150°C
30分鐘@ 150oC額外治愈后建議使用時溫度高于150oC預計。
群眾在0.25grams，讓材料凝膠4小時@ 25oC跟著100oC 5小時
上述固化型材指南建議。 |