化學成份、機械性能、金相組織
序號 種類 牌號 化學成份 機械性能 金相組織
C Si Mn Cr Mo Ni Cu S P Ak
(J/cm2) HRC σb
(Mpa)
1 中碳中鉻Ⅰ ZG30Cr5MoRE 0.25-0.35 0.3-1.0 0.3-1.0 4.5-5.5 0.2-1.0 ≤0.045 ≤0.045 ≥25 ≥45 M+B+C
2 中碳中鉻Ⅱ ZG40Cr5MoRE 0.35-0.45 0.3-1.0 0.3-1.0 4.5-5.5 0.2-1.0 ≤0.045 ≤0.045 ≥20 ≥48 M+B+C
3 中碳低合金 ZG40CrMoNiRE 0.3-0.5 0.7-1.5 0.3-1.0 1.2-1.8 0.2-0.6 0.1-0.4 ≤0.04 ≤0.04 ≥30 ≥40 M+F
4 低碳高合金 ZG20Cr9NiMo 0.15-3.5 ≤1.0 0.3-1.0 8-10 0.4-0.8 1.4-1.8 ≤0.1 ≤0.045 ≤0.045 ≥40 ≥40 M+C
5 鉻鉬鎳合金鋼 ZG45Cr3NiMoMn-RE 0.4-0.50 0.3-0.8 0.6-1.2 2.0-3.2 0.3-0.5 0.5-1.0 ≤0.04 ≤0.04 ≥20 ≥50 M+C
6 90鉻合金鋼 ZG90Cr6MoMn 0.85-0.95 0.4-0.8 0.4-0.8 5-8 0.2-0.4 ≤0.045 ≤0.045 ≥7 ≥50 M+C
7 普通高猛鋼 ZGMn13 1.1-1.4 0.3-1.0 11-14 ≤0.06 ≤0.10 ≥147 HB
≤229 637 A+C
8 改性高錳鋼 ZGMn13Cr2 1.1-1.4 0.3-1.0 11-14 0.5-2.5 ≤0.06 ≤0.10 ≥80 ≤240 A+C
9 超高錳鋼 ZGMn17Cr2 1.1-1.4 0.3-1.0 16-19 1.0-2.0 Ti0.2-0.4 ≤0.06 ≤0.10 ≥50 ≤260 A+C
10 耐熱鋼 ZG20Cr26Ni5 ≤0.20 ≤2.0 ≤0.2 24-28 ≤0.5 4-6 ≤0.04 ≤0.04 590 A+F
11 HH ZG20Cr26Ni12 0.2-0.5 ≤2.0 ≤0.2 24-28 ≤0.5 11-14 ≤0.045 ≤0.045 490 A+F
12 HK ZG40Cr25Ni20 0.35-0.45 ≤2.0 ≤0.2 23-27 ≤0.5 19-22 ≤0.045 ≤0.045 440 A+F
13 高鉻鑄鐵 KmTBCr15Mo2 2-2.8 ≤1.2 0.5-1.0 13-18 0.2-2.5 0-1.0 0-1.2 ≤0.06 ≤0.10 ≥53 M+A+C
14 高鉻鑄鐵 KmTBCr20Mo2 2-3.0 ≤1.2 0.5-1.0 18-22 1.5-2.5 0-1.5 0.8-1.2 ≤0.06 ≤0.10 ≥3 ≥58 M+A+C
15 高鉻鑄鐵 KmTBCr26 2-3.0 ≤1.2 0.5-1.0 23-28 0-1.0 0-1.5 0-2.0 ≤0.06 ≤0.10 ≥55 M+A+C
16 高鉻鑄鋼 ZGCr12SiMn-GT 1.0-2.0 ≤1.2 0.5-2.0 12-14 0-1.0 0-1.0 0-1.0 ≤0.06 ≤0.10 ≥3.2 ≥55 M+A+C
17 高鉻鑄鋼 ZGCr15SiMn-GT 1.0-2.0 ≤1.2 0.5-2.0 15-17 0-1.0 0-1.0 0-1.0 ≤0.06 ≤0.10 ≥3.5 ≥55 M+A+C |
 |
|