樂泰 HYSOL KL 7000HA epoxy molding compounddelivers outstanding performance and ease of use. Thismaterial is designed to achieve JEDEC Level 3 requirements,
at 260°C reflow temperature.樂泰 HYSOL KL 7000HA meets UL 94 V-0 Flammability
at 3.175mm thickness.TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 30Spiral Flow, @ 175°C, cm 110Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATAHandlingPreheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:
Conventional mold, seconds 10 to 25Automold, seconds 4 to 15Curing Time, @ 175oC, seconds:Conventional mold, 70 to 120Automold, 60 to 120Post Cure @ 175°C, hours 4 to 6
StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers. After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination. The suggested waiting time for a standard 15 kg carton box is 24 hours.
樂泰 HYSOL KL 7000HA環氧樹脂成型復合材料具有出色的性能和易用性。
該材料旨在實現JEDEC 3級要求，在260°C回流溫度下.樂泰 HYSOL KL 7000HA符合UL 94 V-0易燃性厚度為3.175mm。固化材料的特性時間175℃，秒30螺旋流，@ 175℃，厘米110秒壽命：@ 5℃，天365工藝過程數據處理預熱溫度：常規模具，80至100Automold，秒0至5模具溫度，°C 150至195模壓，Kg /cm240至100
轉印時間：常規模具，秒10至25Automold，秒4至15固化時間，@175oC，秒：常規模具，70至120Automold，60至120固化175℃，小時4至6StorageStore產品在未開封的容器中，在干燥的位置。存儲信息可能在產品容器標簽上指示。粉末儲存 - 粉末或預制件應存放在5oC以下，密閉容器中。
從冷藏箱中取出后，必須在密封容器中使材料達到室溫，以避免水分污染。標準15公斤紙箱的建議等待時間為24小時。 |