樂泰 HYSOL KL 6500S epoxy molding compound deliversoutstanding performance and ease of use.
This material isdesigned to achieve JEDEC Level 1 requirements, at 260°Creflow temperature.
樂泰 HYSOL KL 6500S meets UL 94 V-0 Flammability at3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 28
Spiral Flow, @ 175°C, cm 110Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATAHandling
Preheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:
Conventional mold, seconds 10 to 24Automold, seconds 4 to 15Curing Time, @ 175oC, seconds:Conventional mold, 60 to 120Automold, 50 to 90Post Cure @ 175°C, hours 4 to 6
StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.
Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers.
After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.
樂泰 HYSOL KL 6500S環氧樹脂模塑復合材料具有出色的性能和易用性。
該材料設計為在260°C達到JEDEC 1級要求回流溫度.樂泰 HYSOL KL 6500S符合UL 94 V-0厚度為1.1775mm的可燃性。
固化材料的特性特性時間@ 175°C，秒28螺旋流，@ 175°C，cm 110Shelf壽命：@5oC，天365工藝流程數據處理預熱溫度：常規模具，℃80至100Automold，秒0至5模具溫度，℃150至195壓鑄壓力，Kg /cm240至100轉印時間：
常規模具，秒10至24Automold，秒4至15固化時間，@175oC，秒：常規模具，60至120Automold，50至90固化175℃，小時4至6StorageStore產品在未開封的容器中，在干燥的位置。
存儲信息可能在產品容器標簽上指示。
粉末儲存 - 粉末或預制件應存放在5oC以下，密閉容器中。
從冷藏箱中取出后，必須在密封容器中使材料達到室溫，以避免水分污染。
標準15kg紙箱的建議等待時間為24小時 |
 |
|