樂泰 HYSOL GR 360A(FC) epoxy molding compounddelivers outstanding performance and ease of use.
樂泰HYSOL GR 360A(FC) epoxy molding compound contains nobromine, antimony or phosphorus flame retardant.樂泰 HYSOL GR 360A(FC) meets UL 94 V-0 Flammabilityat 6.35mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 23Spiral Flow, @ 175°C, cm 73.66Shelf Life:@ 5oC, months 12
Hot Hardness,Shore-D@ 175°C, 90 seconds 85TYPICAL PROCESS DATAHandlingPreheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 20Automold, seconds 4 to 10Curing Time, :Conventional mold:@ 175°C, seconds 40 to 90
Automold:@ 175°C, seconds 20 to 60Post Cure @ 175°C, hours 4 to 6
樂泰 HYSOL GR 360A（FC）環氧樹脂成型復合材料具有出色的性能和易用性。
樂泰HYSOL GR 360A（FC）環氧樹脂模塑料含有無溴，銻或磷阻燃劑.
樂泰 HYSOL GR 360A（FC）符合UL 94 V-0 Flammabilityat 6.35mm厚度。固化材料的特性特性時間@ 175°C，秒23螺旋流，@ 175°C，cm 73.66Shelf壽命：@5oC，月12熱硬度，肖氏-D @ 175°C，90秒85特殊工藝數據處理預熱溫度：常規模具，°C 80至100Automold，秒0至5模具溫度，℃150至195模壓，Kg / cm 2 40至100轉印時間：常規模具秒10〜20Automold，秒4〜10℃時間：常規模具：@ 175℃，秒40〜90秒Automold：@ 175°C，秒20至60℃固化@ 175°C，4至6小時 |
 |
|