樂泰 HYSOL KL 1000-3LXP provides the lowest cost ofownership with superior moldability and reliability.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 27Spiral Flow, @ 175°C, inch 33Shelf Life @ 5oC, months 12Specific Gravity 2.04TYPICAL PROCESS DATAHandlingPreheat Temperature , °C 80 to 90Molding Temperature, °C 170 to 190Transfer Pressure, Kgf/cm2 40 to 85Transfer Time, seconds 5 to 10Curing Time, 3 mm section:@ 175oC 50 to 90樂泰 HYSOL KL 1000-3LXP has been formulated to provide thebest possible moldability and as wide a molding latitude as possible.Although molding and curing conditions will vary from situation tosituation, recommended starting ranges are shown above.
TYPICAL PROPERTIES OF CURED MATERIALAll measurements taken at 25 °C unless otherwise noted.
All physical,electrical and analytical measurements taken on specimens curedfor 2 minutes @ 175 °C with post cure of 6 hours at 175 °C, unlessother wise specified
樂泰 HYSOL KL 1000-3LXP提供*低的擁有成本，具有優(yōu)異的成型性和可靠性。
固化材料的特性特性時間@ 175°C秒秒27螺旋流@ 175°C，英寸33Shelf壽命@5oC，月12特殊重力2.04特殊工藝數據處理預熱溫度，°C 80至90模具溫度，°C 170至190轉印壓力，Kgf /cm240至85轉印時間，秒5至10℃，3 mm截面：@175oC50至90LOCTI HYSOL KL 1000-3LXP已配制成*佳可能的成型性和盡可能寬的成型緯度。
盡管成型和固化條件將根據不同情況而有所不同，但推薦的起始范圍如上所示。固化材料的特性除非另有說明，否則在25°C下進行所有測量。
所有物理，電學和分析測量在175℃下固化2分鐘，175℃下固化6小時， |
 |
|