PRODUCT DESCRIPTION 樂泰® UK U-09FL is a low-viscosity, industrial grade urethane adhesive. Once mixed, the two-component urethane cures at room temperature to form an ultra-clear, highly flexible bond line, which provides excellent peel strength. TYPICAL APPLICATIONS Ideal for bonding polycarbonate, and a variety of other plastics, as well as glass, and metal. Suited for applications requiring a clear, non-yellowing bond line. PROPERTIES OF UNCURED MATERIAL Resin Typical Value Range Chemical Type Polyisocyanate Appearance Clear liquid Specific Gravity @ 25°C 1.1 1.0 to 1.2 C, mPa.s (cP) 7,800 5,000 to 15,000Viscosity @ 25 C See SDSFlash Point (TCC), Hardener Typical Value Range Chemical Type Polyol Appearance Clear Liquid Specific Gravity @ 25°C 1.00 0.95 to 1.15 C, mPa.s (cP) 1,100 600 to 2,000Viscosity @ 25 C See SDSFlash Point (TCC), Mixture Typical Value Appearance Ultra Clear Specific Gravity @ 25°C 1.0 - 1.2 Mix Ratio (R:H) by Weight 100 to 91 by Volume 1 to 1
樂泰®UK U-09FL是一種低粘度，工業級
聚氨酯膠粘劑。一旦混合，雙組分聚氨酯
在室溫下固化形成超清晰，高度靈活
粘結線，提供優異的剝離強度。
典型應用
適用于粘結聚碳酸酯和各種其他塑料，
以及玻璃和金屬。適合要求的應用
清晰，不變黃的粘結線。
不良材料的性質
樹脂典型
價值范圍
化學型多異氰酸酯
外觀透明液體
比重@ 25°C 1.1 1.0〜1.2
粘度@ 25℃，mPa.s（cP）7,800 5,000至15,000
閃點（TCC），℃見SDS
固化劑典型
價值范圍
化學類型多元醇
外觀透明液體
25°C時的比重1.00 0.95〜1.15
粘度@25C，mPa.s（cP）1,100 600至2,000
閃點（TCC），℃見SDS
混合物典型值
外觀超清晰
比重@ 25°C 1.0 - 1.2
混合比（R：H）重量100〜9 |
 |
|