樂泰® 5623™ is a two-component silicone that will cure at room temperature or at elevated temperatures. After mixing, the material cures quickly to form a clear, very flexible elastomer. TYPICAL PROPERTIES OF UNCURED MATERIAL Part A: Specific Gravity @ 22 °C 0.97 Viscosity, Brookfield, 25 °C, mPa•s (cP): Spindle 3, speed 50 rpm 600 to 1,000LMS Part B: Specific Gravity @ 22 °C 0.97 Viscosity, Brookfield, 25 °C, mPa•s (cP): Spindle 3, speed 50 rpm 600 to 1,000LMS Mixed: Specific Gravity @ 22 °C 0.97 TYPICAL CURING PERFORMANCE Gel Time Gel time, 25 °C, minutes 30 to 100LMS TYPICAL PROPERTIES OF CURED MATERIAL After 30 minutes @ 150 °C Physical Properties: Shore Hardness, ISO 868, Durometer OO 30 to 55LMS Cured for 72 hours @ 22 °C Physical Properties: Refractive Index 1.41 Coefficient of Thermal Conductivity ASTM F 433, W/(m•K) 0.15 Storage Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling. Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
樂泰®5623™是雙組分硅膠，可在室溫或高溫下固化。混合后，材料快速固化，形成透明，非常柔軟的彈性體。固化材料的典型特性部分A：比重@ 22°C 0.97粘度，布魯克菲爾德，25°C，mPa•s（cP）：主軸3，轉速50 rpm 600至1,000LMS部分B：比重@ 22°C 0.97粘度，布魯克菲爾德，25°C，mPa•s（cP）：主軸3，轉速50 rpm 600至1,000LMS混合：22°C比重0.97典型固化性能凝膠時間凝膠時間，25°C，30至100LMS固化材料的典型性能在150°C下30分鐘后物理性能：肖氏硬度，ISO 868，硬度計OO 30至55LMS在22℃下固化72小時物理性能：折射率1.41導熱系數ASTM F 433，W / （m•K）0.15儲存將產品存放在未開封的容器中，干燥處。存儲信息可能在產品容器標簽上顯示。*佳儲存溫度：8°C至21°C。低于8°C或高于28°C的儲存可能會對產品性能產生不利影響。 |
 |
|
手機站
您當前位置是：產品大全 >> 化工 >>
膠粘劑
免責聲明：以上所展示的信息由會員自行提供，內容的真實性、準確性和合法性由發布會員負責，www.qy6.com對此不承擔任何責任。如有侵犯您的權益，請來信通知刪除。
10
聯系信息