樂泰 STYCAST EO 8015 liquid epoxy encapsulant is ideal for potting small components.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity @ 25 °C, mPa∙s (cP) 95,000
Specific Gravity, lbs/gal 1.31
Shelf Life @ -16 °C (from date of manufacture), days 180
Flash Point - See SDS
TYPICAL CURING PERFORMANCE
Gel Time
Gel @ 121oC, 20 gm mass, minutes 10
Recommended Cure Schedule
20 minutes @ 121°C
Alternative Cure Schedule
10 minutes @ 149°C
The above cure profile is a guideline recommendation. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Hardness, Shore D 90
Thermal Conductivity , W/(m-K) 0.216
Electrical Properties
Volume Resistivity, ohm-cm 1×1015
Dielectric Strength, volts/mil 535
Dielectric Constant / Dissipation Factor @ 25 °C:
@ 1 KHz 4.25/0.006
@ 10 KHz 4.25/0.012
TYPICAL PERFORMANCE OF CURED MATERIAL
Shear Strength
Tensile Strength N/mm2 6.9
(psi) (1,000)
Lap Shear Strength :
on Aluminum substrate N/mm2 4.7
(psi) (681)
on Valox substrate N/mm2 2.4
(psi) (350)
on Zytel substrate N/mm2 6.2
(psi) (900)
8015液體環氧密封劑樂泰 stycast EO是理想for把小部件。
uncured材料的典型性能
粘度：25℃，mpa∙s 95000（CP）
比重1.31 /加侖，磅
大陸架的生活”- 16°C（from日期，180天制造）
See SDS閃光點
典型的固化性能
凝膠時間
“121oc凝膠，20分鐘，通用汽車的質量，10
推薦的治療計劃
“121°c 20分鐘
替代治療計劃
“149°c 10分鐘
上述程序簡介是指南推薦。（時間和溫度）的治療條件可以基于顧客體驗瓦里和應用要求，as well as客戶固化設備，爐負荷與實際爐溫度。
典型性能的固化材料
物理性質
邵氏D硬度，90
導熱，W /（mK）0.216
電氣性能
體積電阻率，Ωcm 1×1015
介電強度，伏/毫米535
電介質常數/耗散因子”25°C。
|
 |
|