Teroson EP 1450
TEROSON EP 1450 is an expanding one component, high strength structural foam based on Epoxy. The non cured material is resistant to washing and phosphating solutions in normal use in automotive industry and to electro dip painting. The final part gets its geometric shape i.e. by injection molding. TEROSON EP 1450 will cure while passing the EC-oven.
APPLICATION AREAS
TEROSON EP 1450 must be applied as a preformed part in the body shop. The material increases stiffness, strength, fatigue limits and vibration behavior of vehicle bodies. The part is clipped into hollow cavities.
TECHNICAL DATA
(Typical Test Results)
Uncured
Colour grey
Consistency solid
Density at delivery approx. 1.3 g/cm3
Solids Content
(3 h, 105 °C)
> 99 %
Cured
Recommended curing conditions:
mini: 15 min 155°C (keep)
maxi: 20 min 195°C (keep)
Density after expansion approx. 0.6 g/cm3
Expansion > 100 %
Compression test
Compressive strength > 10 MPa
Compressive modulus > 450 MPa
Lap shear strength
Substrates galvanized steel
Bonding area 20 x 25 mm
Layer thickness 2 mm
Strength > 2 MPa
Glass transition
temperature range
(Tg) DMTA (40 Hz, 2 K/min)
> 100 °C
Corrosion resistance
Salt spray test
(35 °C, salt solution 5 %,
500 hours)
no corrosion, no loss of adhesion
Corrosion test (VDA 621-415) no corrosion, no loss of adhesion
Water absorption
(24 h, 98 % humidity, 40 °C)
< 0.5 % weight increase
In service temperature -30 to 80 °C
泰羅松EP 1450是一個擴展的一個組成部分，基于環氧樹脂高強度結構泡沫。非固化材料對汽車行業的清洗和磷化液具有良好的耐腐蝕性，可用于電涂漆。*后一部分得到其幾何形狀，即注塑成型。泰羅松EP 1450治愈而通過EC爐。
應用領域
泰羅松EP 1450作為預留部分美體小鋪。該材料增加剛度，強度，疲勞極限和振動行為的車身。該部件被夾在空心空腔中。
技術數據
（典型測試結果）
未固化的
顏色灰色
一致性固體
密度約1.3克/厘米3交貨
固體含量
|
 |
|
手機站
您當前位置是：產品大全 >> 化工 >>
膠粘劑
免責聲明：以上所展示的信息由會員自行提供，內容的真實性、準確性和合法性由發布會員負責，www.qy6.com對此不承擔任何責任。如有侵犯您的權益，請來信通知刪除。
10
聯系信息