不銹鋼焊絲簡介：
材質 用途 化學成分 力學能力 線徑（mm） 凈重(kg) 閥芯直徑(mm) 備注
ER304 主要用于焊接18Cr-8Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%
拉伸強度Mpa 1200 0.08-0.45 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER304L 主要用于焊接17Cr-8Ni鋼 C:0.028%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%
拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER308 主要用于焊接19Cr-9Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:20.10% 拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER308L 主要用于焊接20Cr-9Ni鋼 C:0.024%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:20.10%
拉伸強度Mpa 1200 0.8-4.5 5/12.5/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER309 主要用于焊接20Cr-13Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:14.33%
Cr:20.10% 拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER309L 主要用于焊接20Cr-14Ni鋼 C:0.024%
Mn:1.65%
Si:0.42%
Ni:14.33%
Cr:20.10%
拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER309Lsi 主要用于焊接20Cr-14Ni鋼 C:0.024%
Mn:1.65%
Si:1.02%
Ni:14.33%
Cr:20.10% 拉伸強度Mpa1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER321 主要用于焊接16Cr-7Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%Ti0.73 拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER347 主要用于焊接16Cr-9Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:9.33%
Cr:17.10%
（Ta+Nb）（10*C）-10 拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 0 MIG:0.8-1.6
TIG:1.0-4.5
ER347L 主要用于焊接17Cr-9Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:9.33%
Cr:17.10%
（Ta+Nb）（10*C）-10 拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 0 MIG:0.8-1.6
TIG:1.0-4.5
ER316 主要用于焊接16Cr-9Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:17.10%
Mo2.03 拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER316L 主要用于焊接17Cr-9Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:17.10%
Mo2.03 拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5
ER310 主要用于焊接24Cr-19Ni鋼 C:0.064%
Mn:1.65%
Si:0.42%
Ni:20.33%
Cr:25.10% 拉伸強度Mpa 1200 0.08-4.5 5/10/15/20 100/270/300 MIG:0.8-1.6
TIG:1.0-4.5 |
 |
|